Fortunately, there are several parts of design such as hinges, fiber optic connector bases, and new style connectors are closely dependent on MIM technology. These products are being produced in a large number and MIM technology is being adopted by more and more.
MIM and CIM--Drome can provide one-stop service solution.
The basic attributes include:
1.Economical production of complex parts with weight from 0.03 to 200g from high-performance engineering materials.
2.Parts with high dimensional precision (±0.1%~±0.5%) and good surface quality (surface roughness 1~2μm).
3.Parts with high relative density (96%~100%), homogeneous microstructure and superior performance.
4.Adaptable to powders of various materials and wide application of the parts.
5.Material saving through the recycle of wastes, production process with high level of automation and suitable for mass production
Flow chart of metal injection molding
Application of MIM
Products Range:
Â
| Material | Â | Typical Values | Â | Â | ||||
| Designation Code | Density g/cm3 | Tensile Properties | Young's modulus, Gpa | Un-notched Charpy Impact Energy,J | Hardness,Rockwell | |||
| Â | Â | UTS. Mpa | Y.S. (0.2%), Mpa | Elongation (in 25.4mm) % | Â | Â | Macro (apparent) | Â Micro (converted) |
| MIM-Fe2Ni | 7.8 | 280 | 115 | 25 | Â | Â | 55 HRB | 50HRCÂ Â Â Â |
| MIM-Fe8Ni | 7.8 | 450 | Â | 12 | Â | Â | 84HRB | 50HRCÂ Â Â Â |
| MIM-2200 (as sintered) | 7.8 | 290 | 125 | 40.0 | 190 | 135 | 45 HRB | Â |
| MIM-2700 (as sintered) | 7.8 | 415 | 255 | 26.0 | 190 | 175 | 69 HRB | Â |
| MIM-4605 (as sintered) | 7.8 | 440 | 205 | 15.0 | 200 | 70 | 62 HRB | Â |
| MIM-4605 (Q&T) | 7.8 | 1655 | 1480 | 2.0 | 205 | 55 | 48 HRC | 55 HRC |
| MIM-304L | 7.8 | 500 | Â | 70 | Â | Â | 60 HRB | Â |
| MIM-316L (as sintered) | 7.85 | 520 | 175 | 50.0 | 190 | 190 | 67 HRB | Â |
| MIM-410 | 7.7 | 900 | Â | 7 | Â | Â | Â | 40 HRC |
| MIM-420 (heat treated) | 7.7 | 1380 | 1200 | 12 | 190 | 40 | Â | 45-60HRC |
| MIM-430L (as sintered) | 7.8 | 410 | 240 | 25.0 | 210 | 150 | 65 HRB | Â |
| MIM-440C | 7.8 | 700 | 590 | 15 | Â | Â | Â | 45-60HRC |
| MIM-17-4PH (as sintered) | 7.8 | 900 | 730 | 6.0 | 190 | 140 | 27 HRC | Â |
| MIM-17-4PH (heat treated) | 7.8 | 1190 | 1090 | 6.0 | 190 | 140 | The forced circulation pump does not rely on the centrifugal force of the impeller to the liquid, but uses the thrust of the rotating impeller blades to make the sent liquid flow along the direction of the pump axis. When the pump shaft is driven by the motor to rotate, because the blade has a certain helix angle with the axis of the pump shaft, a thrust (or lift) is generated on the liquid, and the liquid is pushed out and discharged along the discharge pipe. When the liquid is pushed out, a partial vacuum is formed at the original position, and the liquid outside will be sucked into the impeller along the inlet pipe under the action of atmospheric pressure. As long as the impeller keeps rotating, the pump can continuously suck in and discharge liquid. The forced circulation pump works by using the horizontal thrust along the direction of the pump axis generated by the rotation of the impeller, so it is also called a horizontal axial flow pump. Mainly used in the evaporation of diaphragm method caustic soda, phosphoric acid, vacuum salt production, lactic acid, calcium lactate, alumina, titanium dioxide, calcium chloride, ammonium chloride, sodium chlorate, sugar, molten salt, paper, waste water and other industries. Concentration and cooling, in order to improve the production capacity of the equipment, increase the heat transfer coefficient of the heat exchanger for forced circulation. Therefore, it can also be called an axial flow evaporative circulation pump. Forced Circulation Pump,Circulation Pump,Recirculating Pump,Centrifugal Pumps Jiangsu Qiantu Trading Co., Ltd. , https://www.pumpqt.com | |